Analys av Nedbrytningsprodukter av Polymerer för Bitumenändamål
This project was aimed to study the degradation of polystyrene-butadiene-styrene block copolymer (SBS). SBS is used to modify bitumen, the binder in asphalt. From earlier studies it is known that SBS degrades in bitumen, but the degradation products have not been identified. To be able to determine the long term effects of SBS in the environment, degradation products need to be identified. Polystyrene forms rigid blocks with polybutadiene as a rubbery matrix between the ridgid blocks. When blended in bitumen, the polystyrene blocks are crosslinked to form a three dimensional network. SBS is an elastomer and has the ability to regain its shape after being a subject of mechanical force. According to the pre references the polymers had to be degraded in similar ways as they would in bitumen. Since bitumen is a very complex matrix with high boiling point and viscosity, there would be difficulties separating polymers from the bitumen. We made an assumption that it would be plausible for the degradation products formed in bitumen to form even with no bitumen present. Four different SBS polymers were used. One of the polymers was branched. Another had a high content of 1-2 polybutadiene. The third was a diblock copolymer (SB) with low styrene content compared to the others. The last was a linear SBS. The polymers were degraded in pieces of apparatus used for study ageing characteristics of bitumen as well as they were aged by refluxing in hexane. The degradation products were extracted by Solid Phase Extraction (SPE) and identified by GC-MS. Due to instrumental limits there were not many degradation products identified. The main products detected included saturated hydrocarbons in the range of 16-31 carbon atoms as well as squalene.